High gloss paper 180gsm on SP123 super-permanent adhesive and white kraft liner 80gsm..
Facestock
High Gloss 180
Cast coated woodfree paper.
Technical data
| Property | Norm | Units | Value | Tolerance |
| Substance | ISO 536 | g/m² | 180 | ± 4% |
| Thickness | ISO 534 | µm | 186 | ± 5% |
| Bekk smoothness | ISO 5627 | s | 1050 | ≥ 400 |
| Brightness ISO | ISO 2470-2 | % | 88 | ± 2 |
| Whiteness CIE | ISO 11475 | % | 108 | ± 5 |
| Paper gloss | Tappi T4801 om-92 | % | 44 | ± 5 |
| Opacity | ISO 2471 | % | 99 | -2 |
| Tensile strength MD/CD | ISO 1924-2 | kN/m | 6.5/3.6 | -0.6/-0.3 |
Notes
-
Values are subject to change without notice.
Last updated 1/1/2024
-
The technical information that appears in this document reflects our knowledge and experience, but should only be considered as a general guideline
Adhesive
SP123
Acrylic super-permanent adhesive with high tack. For difficult surfaces such as wood, some cardboards and plastics such as HDPE, PP, PET and PVC.
Technical data
| Property | Norm | Units | Value | Tolerance |
| Adhesion (Peel 180º 20'/stainless steel) | FTM 1 | N/25mm | 17,2 | ≥ 13,5 |
| Tack (Quick Stick stainless steel) | FTM 9 | N | 11 | ≥ 9,8 |
| Shear (1kg, in²/glass) | FTM 8 | min | 100 | ≥ 60 |
| Minimum labelling temperature | | ºC | +5 | |
| Minimum service temperature | | ºC | -20 | |
| Maximum service temperature. | | ºC | +80 | |
Notes
-
Values are subject to change without notice.
Last updated 1/1/2024
-
The technical information that appears in this document reflects our knowledge and experience, but should only be considered as a general guideline
Liner
Kraft White 80
One-side coated white liner with good lay-flat characteristics. Suitable for sheeting. Available only in solid back
Technical data
| Property | Norm | Units | Value | Tolerance |
| Substance | ISO 536 | g/m² | 80 | ± 4% |
| Thickness | ISO 534 | µm | 81 | ± 4 |
| Tensile strength MD/CD | ISO 1924-2 | kN/m | 4,6/2,3 | -0,6/-0,3 |
Notes
-
Values are subject to change without notice.
Last updated 1/1/2024
-
The technical information that appears in this document reflects our knowledge and experience, but should only be considered as a general guideline